HDPE Tr144
Mã Sản Phẩm: HDPE Tr144
Description
This high molecular weight, hexene copolymer is tailored for blown film applications that require:
Toughness and durability
Good processability
Good blending characteristics with HDPE HMW resins
Melt Flow Index (MI)
0.18
Material Grou
HPDE Film
Producer
MALEX
Origin
Arabic
Application
Shopping bag
This resin meets these specifications:
- FDA 21 CFR 177.1520(c) 3.2a
- EU No. 10/2011
Typical applications for HHM TR-144 include:
- T-shirt bags
- Multi-wall liners
- Trash bags
Properties
Values
Units SI
Test methods
Polymer properties
Melt flow rate (MFR) at 190 °C and 2.16 kg
Density
Brittleness Temperature, Type A clamp, Type I specimen
ESCR, Condition B (100% Igepal), F50
Flexural Modulus, Tangent - 16:1 span:depth, 12.7 mm/min
g/10 min
g/cm³
<-75°C
>1000 hrs
1150 MPa
ASTM D1505
ASTM D1238
ASTM D746
ASTM D1693
ASTM D790
Nominal Blown Film Properties at 0.025mm
0.18
0.946
Dart Drop (66 cm)
Tensile Strength at Yield, 50.8 mm/min MD
Tensile Strength at Yield, 50.8 mm/min TD
Elongation at Break, 50.8 mm/min MD
Elongation at Break, 50.8 mm/min TD
Elmendorf Tear Strength, MD
Elmendorf Tear Strength, TD
g
MPa
MPa
%
%
g
g
90
24
26
480
640
19
270
ASTM D1709
ASTM D882
ASTM D882
ASTM D882
ASTM D882
ASTM D1922
ASTM D1922
1. The nominal properties reported herein are typical of the product, but do not reflect normal testing variance and therefore should not be used for specification purposes. Values are rounded.
2. The physical properties were determined on compression moulded specimens that were prepared in accordance with Procedure C of ASTM D4703, Annex A1.
3. Based on 0.025 mm film produced at 4:1 blow-up ratio